Engineering Center and Manufacturing of Solid Adsorbents and Catalysts, Iranian Institute of Research and Development in Chemical Industries (IRDCI)-ACECR, Karaj, I.R. IRAN
Abstract
In this study alumina powder was synthesized by precipitation method. Boehmite gel was produced by hydrolysis of aluminium nitrate at pH rang of 8-9 and temperature of 90°C. The obtained gel was dried at 110°C and extruded subsequently. Extrudes were dried and calcined at 600°C. The final product has a surface area of > 200 m2/g and mean pore diameter of 6.6-11.63 nm. The γ- alumina extrudates were then wet impregnated with molybdenium and cobalt salts, respectively. To produce γ-alumina supported CoMo catalyst (CoMo/γ-alumina). The amount of impregnated metal was measured by XRF technique. TPR analysis was performed to determine the reduction power.
Shahidian,Z and Papan,A . (2014). Effect of pH Parameter on the Synthesis of CoMo/γ- Alumina Catalyst Prepared from Extruded Boehmite Based γ-Alumina by Using Precipitation. Nashrieh Shimi va Mohandesi Shimi Iran, 33(4), 53-60.
MLA
Shahidian,Z , and Papan,A . "Effect of pH Parameter on the Synthesis of CoMo/γ- Alumina Catalyst Prepared from Extruded Boehmite Based γ-Alumina by Using Precipitation", Nashrieh Shimi va Mohandesi Shimi Iran, 33, 4, 2014, 53-60.
HARVARD
Shahidian Z, Papan A. (2014). 'Effect of pH Parameter on the Synthesis of CoMo/γ- Alumina Catalyst Prepared from Extruded Boehmite Based γ-Alumina by Using Precipitation', Nashrieh Shimi va Mohandesi Shimi Iran, 33(4), pp. 53-60.
CHICAGO
Z Shahidian and A Papan, "Effect of pH Parameter on the Synthesis of CoMo/γ- Alumina Catalyst Prepared from Extruded Boehmite Based γ-Alumina by Using Precipitation," Nashrieh Shimi va Mohandesi Shimi Iran, 33 4 (2014): 53-60,
VANCOUVER
Shahidian Z, Papan A. Effect of pH Parameter on the Synthesis of CoMo/γ- Alumina Catalyst Prepared from Extruded Boehmite Based γ-Alumina by Using Precipitation. NSMSI. 2014;33(4):53-60 (In Persian).