Manufacturing a Supercritical Carbon Dioxide Dryer and its Application for Production of Nickel (II) Oxide Aerogel

Document Type : Research Article

Authors
Elahe Babaei
Amin Bazyari
Department of Chemical Engineering, Oil and Gas, Iran University of Science and Technology, Tehran, IRAN
Abstract
In this research, a simple supercritical carbon dioxide dryer was designed and constructed for the production of various aerogels. The most significant advantage of the constructed device was its automatic heating and cooling system, which allowed better control of the operational conditions during the drying process and the production of nanostructured materials with increased porosity. The constructed device had the capability to operate in a temperature range of 5°C to 90°C and pressures up to 140 bar. To evaluate the performance of the constructed device, nickel oxide (II) gel was synthesized using the sol-gel method and dried using the supercritical carbon dioxide drying method. The prepared aerogel was calcined at a temperature of 300°C for 2 hours. The physical and chemical characteristics of the nickel oxide aerogel were examined using X-ray diffraction (XRD) analysis, Brunauer-Emmett-Teller (BET) nitrogen adsorption and desorption, and field emission scanning electron microscopy (FESEM). The results indicated that the nickel oxide aerogel had an open porous structure and was composed of spherical nanoparticles. The synthesized aerogel had a specific surface area of 167 m²/g, pore volume of 0.61 cm³/g, average pore diameter of 6.14 nm, and average crystallite size of 6.4 nm. The obtained results demonstrated that drying nickel oxide nanostructures using the constructed supercritical carbon dioxide dryer led to better preservation of its porous structure.
Keywords
Supercritical Dryer
Supercritical Carbon Dioxide
Aerogel
Nickel Oxide
Nanoparticle

Subjects

[1] Moral M., Rueda M., Mato R., Martín Á., View Cell Investigation of Silica Aerogels during Supercritical Drying: Analysis of Size Variation and Mass Transfer Mechanisms, Supercritical Fluids, 92: 24-30 (2014).
[2] Mißfeldt F., Gurikov P., Lölsberg W., Weinrich D., Lied F., Fricke M., Smirnova I., Continuous Supercritical Drying of Aerogel Particles: Proof of Concept, Ind. Eng. Chem. Res, 59: 11284-11295 (2020).
[3] Stergar J., Maver1U., Review of Aerogel-Based Materials in Biomedical Applications, Sol-Gel Science and Technology, 77: 738-752 (2016).
[4] Ziegler C., Wolf A., Liu W., Herrmann A., Gaponik N., Eychmgller A., Modern Inorganic Aerogels, Angew.Chem. Int. Ed, 56: 13200-13221 (2017).
[5] Kawagishi K., Saito H., Furukawa H., Horie K., Superior Nanoporous Polyimides via Supercritical CO2 Drying of Jungle-Gym-Type Polyimide Gels, Macromol. Rapid Commun, 28: 96-100 (2007).
[6] García-Gonzáleza C., Camino-Reya M., Alnaiefb M., Zetzla C., Smirnovaa I., Supercritical Drying of Aerogels using CO2: Effect of Extraction Time on the End Material Textural Properties, Supercritical Fluids, 66: 297-306 (2012).
[7] Ganesan K., Budtova T., Ratke L., Gurikov P., Baudron V., Preibisch I., Niemeyer P., Smirnova I., Milow B., Review on the Production of Polysaccharide Aerogel Particles, Materials, 11(11): 2144 (2018).
[8] Barrios J., Calderon E., Nanomaterials in Advanced, High-Performance Aerogel Composites: A Review, Polymers, 11(4): 726 (2019).
[9] Smirnova I., Gurikov P., Aerogels in Chemical Engineering : Strategies Toward Tailor-Made Aerogels, Review of Chemical and Biomolecular Engineering, 8: 307-334 (2017).
[10] Sui R., Charpentier P., Synthesis of Metal Oxide Nanostructures by Direct Sol−Gel Chemistry in Supercritical Fluids, Chem. Rev., 112: 3057-3082 (2012).
[11] Bommel M., Haan A., Drying of Silica Gels With Supercritical Carbon Dioxide, Materials Science, 29: 943-948 (1994).
[12] Gash A., Satcher J., Simpson J., Monolithic Nickel (II)-Based Aerogels Using an Organic Epoxide: The Importance of the Counterion, Non-Crystalline Solids, 350: 145-151 (2004).
[13] Wu M., Gao J., Zhang S., Chen A., Synthesis and Characterization of Aerogel-Like Mesoporous Nickel Oxide for Electrochemical Supercapacitors, Porous Mater, 13: 407-412 (2006).
[14] Haitao L., “Supercritical Carbon Dioxide Aided Preparation of Nickel Oxide/Alumina Aerogel Catalyst”, Annual Accountability Report, Graduate Theses and Dissertations, 32 (2005).
[15] Dissertations D., Hana Y., Yanga H., Shena C., Zhoua X., Wanga F., Synthesis and Size Control of NiO Nanoparticles by Water-in-Oil Microemulsion, Powder Technology, 147: 113-116 (2004).
[16] Kazemi H., Shahhosseini S., Bazyari A., Amiri M., "A study on the effects of textural properties of γ-Al2O3 support on CO2 capture capacity of Na2CO3 ", J. Process Safety and Environmental Protection, 138: 176-185 (2020).
[17] Arvaneh R., Fard A. A., Bazyari A., Alavi S. M., Abnavi F. J., "Effects of Ce, La, Cu, and Fe promoters on Ni/MgAl2O4 catalysts in steam reforming of propane", J. Korean Journal of Chemical Engineering, 36: 1033-1041 (2019).
[18] Azizzadeh Fard, A., Bazyari, A., Alavi, S. M., Aghamiri, A. R., "The effects of cobalt and cerium promoters on hydrogen production performance of alumina‐supported nickel catalysts in propane steam reforming", J. Chemical Technology & Biotechnology, 95: 3241-3251 (2020).
[19] Zhang Z., Gao Q., Gao H., Shi Z., Wu J., Zhi M., Nickel Oxide Aerogel for High Performance Supercapacitor Electrodes, RSC Adv., 6: 11262 (2016).
[20] Dhas S., Maldar P., Patil M., Nagare A., Waikar M., Sonkawade R., Synthesis of NiO Nanoparticles for Supercapacitor Application as an Efficient Electrode Material, Vacuum, 181: 109646 (2020).