Polyethylene Glycol-Assisted Synthesis of High Specific Surface Area and Pore Volume γ-Al2O3 Using Sol-Gel Method

Document Type : Research Article

Authors
Hossein Kazemi
Shahrokh Shahhosseini
Amin Bazyari
School of Chemical, Petroleum, and Gas Engineering, Iran University of Science and Technology, Tehran, I.R. IRAN
Abstract
In this study, the effects of polyethylene glycol on the structural properties of gamma-alumina (γ-Al2O3) synthesized via a modified sol-gel process was investigated. To this end, polyethylene glycol (PEG) and aluminum isopropoxide (Al(OPri)) were used as the structure-directing agent and aluminum precursor, respectively. Nitrogen adsorption-desorption analysis was performed to obtain the specific surface area, pore-volume, and pore size distributions of the γ-Al2O3 samples synthesized with different mole ratios of PEG/Al(OPri). The maximum specific surface area (344 m2/g) and the pore volume (2.2 cm3/g) was obtained for the γ-Al2O3 prepared with a PEG/Al(OPri) mole ratio of 0.05. These surface area and pore volumes were about 40 and 340% higher than the sample synthesized in the absence of PEG. It was also observed that increasing the mole ratio of PEG/Al(OPri) to more than 0.05 had no significant effect on the structure of γ-Al2O3. The best sample was further studied by Scanning Electron Microscopy (SEM) and X-Ray Diffraction (XRD) analyses and the results were compared with the commercial γ-Al2O3 prepared from Merck Company with a specific surface area and pore volume of 174 m2/g and 0.5 cm3/g, respectively. XRD analysis showed that the crystallite sizes of the best-synthesized sample and Merck product were 7 and 13 nm, respectively. Unlike previous γ-Al2O3 synthesis methods, in which synthetic samples with a high specific surface area typically had a small pore volume, the use of PEG in the sol-gel process could significantly increase both the specific surface area and the pore volume. Furthermore, PEG-assisted synthesis of γ -Al2O3 was less complex than the other methods.
Keywords
Sol-gel
γ-alumina
Polyethylene glycol
Specific surface area
Pore volume

Subjects

[1] Sengupta S., Amte V., Dongara R., Das A.K., Bhunia H., Bajpai P.K., Effects of the Adsorbent Preparation Method for CO2 Capture from Flue Gas Using K2CO3/Al2CO3 Adsorbents, Energy Fuels, 29(1): 287-297 (2015).
 [2] Kajohnchaiyagual J., Jubsilp C., Dueramae I., Rimdusit S., Thermal and Mechanical Properties Enhancement Obtained in Highly Filled Alumina‐Polybenzoxazine Composites, Polymer Composites, 35(11): 2269-79 (2014).
[3] Jain S., Bansiwal A., Biniwale R.B., Milmille S., Das S., Tiwari S., Antony P.S., Enhancing Adsorption of Nitrate Using Metal Impregnated Alumina, Environmental Chemical Engineering, 3(4): 2342-9 (2015).
[4] Santos P.S., Santos H.S., Toledo S., Standard Transition Aluminas. Electron Microscopy Studies, Materials Research, 3(4): 104-14 (2000).
[5] Dong W., Chen X., Yu F., Wu Y., Na2CO3/MgO/Al2CO3 Solid Sorbents for Low-Temperature CO2 Capture, Energy Fuels, 29(2): 968-973 (2015).
[6] Paglia G., Rohl AL., Buckley C.E., Gale J.D., Determination of the Structure of γ-alumina from Interatomic Potential and First-Principles Calculations: The Requirement of Significant Numbers of Nonspinel Positions to Achieve an Accurate Structural Model, Physical Review B, 71(22): 224115 (2005).
[7] Trueba M., Trasatti S.P., γ-Alumina as a Support for Catalysts: A Review of Fundamental Aspects, European Journal of Inorganic Chemistry, (17): 3393-3403 (2005).
[8] Zhang Z., Hicks R.W., Pauly T.R., Pinnavaia T.J., Mesostructured forms of γ-Al2O3, American Chemical Society, 124(8): 1592-3 (2002).
[9] Farias R.F., Arnold U., Martınez L., Schuchardt U., Jannini M.J., Airoldi C., Synthesis, Characterization and Catalytic Properties of Sol-Gel Derived Mixed Oxides, Physics and Chemistry of Solids, 64 (12): 2385-9 (2003).
[10] Teoh G.L., Liew K.Y., Mahmood W.A.K., Synthesis and Characterization of Sol-Gel Alumina Nanofibers, Sol-Gel Science and Technology, 44 (3): 177-186 (2007).
[11] Aguado J., Escola J., Castro M., Paredes B., Sol-Gel Synthesis of Mesostructured γ-alumina Templated by Cationic Surfactants, Microporous and Mesoporous Materials, 83(1): 181-92 (2005).
[12] Lee H.C., Kim H.J., Rhee C.H., Lee K.H., Lee J.S., Chung S.H., Synthesis of Nanostructured γ-Alumina with a Cationic Surfactant and Controlled Amounts of Water, Microporous and Mesoporous Materials, 79 (1): 61-8 (2005).
[13] Sanchez-Valente J., Bokhimi X., Toledo J., Synthesis and Catalytic Properties of Nanostructured Aluminas Obtained by Sol-Gel Method, Applied Catalysis A: General, 264 (2): 175-81 (2004).
[14] Buelna G., Lin Y., Sol–Gel-derived Mesoporous γ-Alumina Granules, Microporous and Mesoporous Materials, 30 (2): 359-69 (1999).
[15] Keshavarz A.R., Rezaei M., Yaripour F., Nanocrystalline Gamma-Alumina: A Highly Active Catalyst for Dimethyl Ether Synthesis, Powder Technology, 199 (2): 176-179 (2010).
[16] Akia M., Alavi S.M., Rezaei M., Yan Z.F., Optimizing the Sol-Gel Parameters on the Synthesis of Mesostructure Nanocrystalline γ-Al2O3, Microporous and Mesoporous Materials, 122 (1): 72-78 (2009).
[17] Tokudome Y., Fujita K., Nakanishi K., Miura K., Hirao K., Synthesis of Monolithic Al2O3 with Well-Defined Macropores and Mesostructured Skeletons via the Sol−Gel Process Accompanied by Phase Separation, Chemistry of Materials, 19 (14): 3393-8 (2007).
[18] Dormidontova E.E., Role of Competitive PEO−Water and Water−Water Hydrogen Bonding in Aqueous Solution PEO Behavior, Macromolecules, 35 (3): 987-1001 (2002).
[19] Passos A., Pulcinelli S., Briois V., Santilli C., High surface Area Hierarchical Porous Al2O3 Prepared by the Integration of Sol-Gel Transition and Phase Separation, RSC Advances, 6 (62): 57217-26 (2016).
 [20] Lamouri S., Hamidouche M., Bouaouadja N., Belhouchet H., Garnier V., Fantozzi G., Trelkat J.F., Control of the γ-Alumina to Α-Alumina Phase Transformation for an Optimized Alumina Densification, Boletín de la Sociedad Española de Cerámica y Vidrio, 56 (2): 47-54 (2017).
[21] Dabbagh H.A., Rasti E., Yalfani M.S., Medina F., Formation of γ-Alumina Nanorods in Presence of Alanine, Materials Research Bulletin, 46 (2): 271-277 (2011).
[22] Sing K.S., Reporting Physisorption Data for Gas/Solid Systems with Special Reference to the Determination of Surface Area and Porosity (Recommendations 1984), Pure and Applied Chemistry, 57 (4): 603-19 (1985).
[23] Thommes M., Smarsly B., Groenewolt M., Ravikovitch P.I., Neimark A.V., Adsorption Hysteresis of Nitrogen and Argon in Pore Networks and Characterization of Novel Micro- and Mesoporous Silicas, Langmuir, 22 (2): 756-64 (2006).
[24] Rouquerol F., Rouquerol J., Sing K., Absorption by Powders and Porous Solids: Principles, Methodology and Applications, First Edition, Academic Press, London (1998).
[25] Bu S., Jin Z., Liu X., Du H., Cheng Z, Preparation and Formation Mechanism of Porous TiO2 Films Using PEG and Alcohol Solvent as Double-Templates, Journal of Sol-Gel Science and Technology, 30 (3): 239-248 (2004).
[26] Liu X., Jin Z., Bu S., Yin T., Influences of Solvent on Properties of TiO2 Porous Films Prepared by a Sol-Gel Method from the System Containing PEG, Journal of Sol-Gel Science and Technology, 36 (1): 103-111 (2005).
[27] Musil J., Blazek J., Zeman P., Proksova S., Sasek M., Cerstvy R., Thermal Stability of Alumina Thin Films Containing -Al2O3 Phase Prepared by Reactive Magnetron Sputtering, Applied Surface Science, 257 (3): 1058-1062 (2010).
[28] Patterson A., The Scherrer Formula for X-Ray Particle Size Determination, Physical Review, 56 (10): 978 (1939).
[29] Myers H.P., “Introductory Solid State Physics”, CRC Press, (1997).