The Use of Hydroxide Precipitation and Reduction Methods in The Separation of Iron, Arsenic, and Antimony Impurities from Leached Solution of Silicate Ore Hemimorphite

Document Type : Research Article

Authors
Akram Ram
Saeid Zandevakili
Department of Mineral Materials Processing, Department of Mining Engineering, Veli-e- Asr University, Rafsanjan. I.R. IRAN
Abstract
The purpose of this research is to separate iron, arsenic and antimony impurities from zinc silicate ore leach solution using precipitation methods including hydroxide precipitation, by changing pH and reduction precipitation, by changing oxidation/reduction potential. The optimum condition to remove impurities with minimal zinc loss, achieved in the presence of Ca(OH)2, pH = 4.5, temperature of 70°C, in 40 minutes by hydroxide precipitation, and 0.5g/liter of zinc powder, 60°C and 60 minutes by reduction precipitation. In these conditions, most of the main impurities, including 98% iron and arsenic ions, more than 80% of antimony ions and approximately 60.5% of copper ions, were removed. Furthermore, in these conditions, only 5.63% of zinc ions were lost. Therefore, the most part of PLS impurities, were removed before solvent extraction, by performing a successive pre-purification. The results showed that the pH parameter and the precipitant agent had the greatest effect on the precipitation process.
Keywords
Zinc
Hydroxide precipitation
Reductive precipitation
Taguchi design expert

Subjects

 [1] شمسی، مصطفی؛ نوع پرست، محمد؛ تقوی ، سید مصطفی؛ پرعیارسازی و تولید روی از طریق حذف ناخالصی­ های  PLS حاوی این فلز، دومین همایش ملی سرب و روی ایران، زنجان، (1393).
[2] Chang Y., Xiujing Z., Binchuan L., Yan F., Removal of Iron from Acidic leach liquor of Lateritic Nickel Ore  By Goethite Precipitate, Hydrometallurgy, 101: 84-87 (2009).
[3] خداکرمی، مصطفی؛ بررسی استحصال کبالت و منگنز از پسماند کارخانجات تولید روی به روش هیدرومتالورژی (ترسیب و تبادل)، پایان نامه ارشد، دانشکده فنی مهندسی گروه مهندسی معدن، دانشگاه بین­المللی امام خمینی(ره)، (1393).
[4] Brboot M., Balasim A.,  Altameemi A., Al-Shuwaik N., Removal of Heavy Metals Using Chemicals Precipitation , Eng.& Tech. Journal. 29(3): (2011).
[5] Kamran Haghighi H., Moradkhani  D., Sedaghat B., Rajaie Najafabadi M., Behnamfard  A.,  Production of Copper Cathode from Oxidized Copper Ores by Acidic Leaching and two-step Precipitation followed by Electrowinning,  Hydrometallurgy, 133: 111-117 (2013).
[6] Zhang Y., Feng  X., Jin B., An effective Separation Process of Arsenic, Lead and Zinc from High Arsenic-Containing Copper Smelting ashes by Alkali Leaching followed by Sulfide Precipitation , Waste Management & Research, 1–8 (2020).
[7]. Yang Z., Zhang Y., Zhou H., Luo X., Tang X., Liu Z., Selective Separation Recovery of Copper and Arsenic from the Leaching Solution of Copper Soot, Metals, 12: 1983 (2022).
[8] کچویی، عطیه سادات؛ امکان سنجی جداسازی فلزات با ارزش مس، کبالت و نیکل از محلول­ های باطله غلظت پایین، پایان نامه ارشد، دانشکده مهندسی شیمی، دانشگاه صنعتی اصفهان، (1393).
[9] اثیمی نیسیانی، علی؛ غریبی، خداکرم؛ آبخشک، عماد؛ تاثیر پارامترهای مختلف بر ترسیب آهن سه ظرفیتی در کارخانه ذوب روی بافق، کنفرانس ملی مهندسی مواد، متالورژی و معدن ایران، اهواز، (1396).
[10] یوسفی، فاطمه؛ استحصال فلز روی از باطله های کم عیار اکسید روی معدن باما با روش لیچینگ و استخراج حلالی، پایان نامه ارشد، دانشکده فنی مهندسی، گروه مهندسی معدن، دانشگاه بین المللی امام خمینی (ره)، (1396).
[11] زحمتی، فرزاد؛ شایسته، کیوان؛  وحیدفر، وحید؛ امامقلی لو، زینب؛ مطالعه تاثیر دما بر روی سینتیک واکنش سمنتاسیون نیکل، کادمیوم و کبالت در محلول سولفات روی، پنجمین کنفرانس علوم و مهندسی جداسازی، (1401).